METALCLAD CeramAlloy HTP

Repair & rebuild all types of equipment – even at elevated temperatures!

METALCLAD CeramAlloy HTP is a two component, 100% solids polymer composite specifically formulated to rebuild and repair all types of fluid flow equipment that may be subject to elevated temperatures.

  • Trowelable
  • Requires No Heat
  • Unlimited Shelf Life
  • 100% Solids
  • Safe & Simple To Use

Repairs and Protects...

  • Heat Exchanger Tube Sheets & Water Boxes
  • Pumps
  • Valves & Pipework
  • Housings & Tanks
  • Drum Dryers
  • Distillation Units
  • Stacks
  • Scrubbers
  • ...and more

Technical Data

Volume capacity per kg.
38 in3 / 629 cc
Mixed density
0.057 lbs per in3 / 1.59 gm per cc
Coverage rate per kg. @ 0.25 in / 6 mm
152 in2 / 0.098 m2
Shelf life
Indefinite
Volume Solids
100%
Mixing ratio Base Activator
By Volume 2.3 1
By Weight 5 2

Working Life and Cure Times

Ambient Temperature Working Life Machining Light Load Full Mechanical Chemical Immersion
59°F 15°C 1.5 hrs 20 hrs. 48 hrs. 5 days
77°F 25°C 40 min. 10 hrs. 18 hrs. 3 days
86°F 30°C 25 min. 7 hrs. 15 hrs. 2 days

Physical Properties

Typical Values Test Method
Compressive strength 12,500 psi 875 kg/cm2 ASTM D-695
Flexural strength 8,500 psi 595 kg/cm2 ASTM D-790
Hardness - Shore D 87  
Tensile Shear Adhesion    
Steel 4000 psi 280 kg/cm2 ASTM D-1002
Copper 2500 psi 175 kg/cm2 ASTM D-1002
Stainless Steel 3500 psi 246 kg/cm2 ASTM D-1002

Chemical Resistance

Ammonia (5%) EX NaCl (5%) EX
HCL (20%) G Sulfuric acid (98%) G
Motor oil EX Sulfuric acid (50%) EX

EX - Suitable for most applications including immersion
G - Suitable for intermittent contact, splashes, etc.

Temperature Guidelines

Up to:

Dry - 520°F / 270°C

Wet - 330°F / 165°C

We would always recommend that elevated temperature applications be discussed with your local ENECON Fluid Flow Systems Specialist.