METALCLAD CeramAlloy CL+AC

Outstanding erosion/corrosion resistance!
Repairs Damaged Equipment - Protects New Components.

The Most Advanced Polymer Composite Coating System Available!

METALCLAD CeramAlloy CL+AC is a 100% solids, two component, liquid polymer composite used for repairing, resurfacing and coating components to provide outstanding fluid flow erosion and corrosion resistance.

When mixed, METALCLAD CeramAlloy CL+AC is a viscous liquid. CL+AC cures to a hard, ceramic-like material with an extremely smooth surface finish.

High Performance Polymer Composite for resurfacing and protecting all types of fluid flow components from aggressive erosion and corrosion damage.

  • Apply by Brush, Roller or Flexible Applicator
  • Requires No Heat
  • Unlimited Shelf Life
  • 100% Solids
  • Safe & Simple To Use

METALCLAD CeramAlloy is qualified for AFFF (aqueous film forming foam) stations and high-traffic interior passageway protection on U.S. Navy vessels as detailed in MIL-PRF-32171 "The material covered by the specification is intended for use as high durability, wear resistant deck coating for use in high traffic areas, with minimal maintenance. The coating may be supplied with or without aggregate


Technical Data

Volume capacity per kg.
36 in3 / 592 cc
Mixed density
0.061 lbs per in3 / 1.69 gm per cc
Coverage rate per kg. @ 12 - 15 mils
14 - 16 ft2 / 1.4 m2
Shelf life
Indefinite
Volume Solids
100%
Mixing ratio Base Activator
By Volume 3.3 1
By Weight 6 1

Colors

Blue

Gray

Note: Other colors are available on a “special order” basis. However, there are minimum / multiple quantity requirements for such orders and there may be an increase in cost. Additionally, due to formulation restrictions, not all colors are possible for all materials. Speak to your local ENECON Sales Representative for more information.

Due to monitor / printer differences, actual colors may vary slightly from the representations appearing in this chart.

Working Life and Cure Times

Ambient Temperature Working Life Machining Light Load Full Mechanical Chemical Immersion
41°F 5°C 4 hrs. 48 hrs. 96 hrs. 10 days
59°F 15°C 2 hrs 24 hrs. 48 hrs. 5 days
77°F 25°C 1 hr 12 hrs. 24 hrs. 3 days
86°F 30°C 40 min. 8 hrs. 20 hrs. 2 days

Physical Properties

Typical Values Test Method
Compressive strength 13,500 psi 945 kg/cm2 ASTM D-695
Flexural strength 8,000 psi 560 kg/cm2 ASTM D-790
Izod impact strength 1.3 ft lbs/in 0.69 j/cm ASTM D-256
Hardness - Shore D 85 ASTM D-2240
Taber Abrasion Resistance    
  CS-17 Wheel, 1000 cycles, 1 Kg Load Dry - 12.5 mm3 loss ASTM D-4060
  H-10 Wheel, 1000 cycles, 1 Kg Load Wet - 160.6 mm3 loss ASTM D-4060
Tensile Shear Adhesion    
Steel 4000 psi 280 kg/cm2 ASTM D-1002
Aluminum 2500 psi 175 kg/cm2 ASTM D-1002
Copper 3000 psi 210 kg/cm2 ASTM D-1002
Stainless Steel 4100 psi 287 kg/cm2 ASTM D-1002
Surface resistivity 1 x 1015 ohms ASTM D-257
Volume resistivity 1 x 1015 ohm/cm ASTM D-257
Dielectric constant 7.5 ASTM D-150
Dielectric strength 652 volts/mil ASTM D-115
Breakdown Voltage 6.1 Kv ASTM D-115

Chemical Resistance

Acetic acid (0-10%) EX Methyl alcohol G
Acetic acid (10-20%) G Methyl ethyl ketone G
Acetone G Nitric acid (0-10%) EX
Aviation fuel EX Nitric acid (10-20%) G
Butyl alcohol EX Phosphoric acid (0-5%) EX
Calcium chloride EX Phosphoric acid (5-10%) G
Crude oil EX Potassium chloride EX
Diesel fuel EX Propyl alcohol EX
Ethyl alcohol G Sodium chloride EX
Gasoline EX Sodium hydroxide EX
Heptane EX Sulfuric acid (0-10%) EX
Hydrochloric acid (0-10%) EX Sulfuric acid (10-20%) G
Hydrochloric acid (10-20%) G Toluene G
Kerosene EX Xylene EX

EX - Suitable for most applications including immersion
G - Suitable for intermittent contact, splashes, etc.

Extended Information

Ask an ENECON Tech

Fill out my online form.

Sign up for ENECON's latest Repair - Don't Replace solution

Fill out my online form.

Case Studies

live chat service provider